研究了用硫酸、FeSO4从氧化铈废料中浸出稀土。结果表明:硫酸及FeSO4加入量、浸出温度及浸出时间对稀土浸出率有一定影响;在硫酸及FeSO4加入量均为理论量的1.4倍、温度50℃、浸出时间1.5h最优条件下,稀土浸出率在80%以上。
Abstract：Leaching of rare earth from waste cerium oxide with sulfuric acid and ferrous sulfate was studied.Experimental results show that the amount of sulfuric acid and ferrous sulfate,leaching temperature and leaching time all affect the recovery of rare earth.The optimum conditions are that the amount of sulfuric acid and ferrous sulfate are the theoretical amount,leaching time is 1.5h,and leaching temperature is 50 ℃.Under the optimum conditions,the recovery rate of rare earth is more than 80%.
[1]ABDELDAYEM H A,FRAZIER D O,PENN B G,et al.Non-linear optothermal properties of metal-free phthalocyanine[J].Thin Solid Films,1999,350(1/2):245-248.
[2]赵于文.超细粉的性能、制备及应用[J].现代化工,1991(5):52-58.
[3]冯丽娟,赵宇靖,陈涌英.超细粒子催化剂[J].石油化工,1991,20(9):633-639.
[4]董相廷,洪广言,于得财.CeO2纳米粒子形成过程中Ce的价态变化[J].硅酸盐学报,1997,25(3):323-327.
[5]田禾,苏建华,孟凡顺,等.功能性色素在高新技术中的应用[M].北京:化学工业出版社,2000:164.
[6]欧阳成,周蓉,荆旭东.微波-超声波协同作用下氧化铈的制备与表征[J].湿法冶金,2014,33(4):305-308.
[7]马光辉,苏志国.新型高分子材料[M].北京:化学工业出版社,2003:249.
[8]PALEY M S,HARRIS J M,LOOSER H,et al,A solvationchromic method for determining second-order polarizabilities of organic molecules[J].J Org Chem,1990,55(5):1692.
[9]李宏煦,王帅,李超.稀土元素回收技术及其生命周期循环分析[C]//中国稀土学会.2015年全国稀土金属冶金工程技术交流会论文集,包头,2015.
[10]李建宁,黄小卫,朱兆武,等.P204-2P507-2H2SO4体系萃取稀土元素的研究[J].中国稀土学报,2007,25(1):55-58.
[11]付文慧,葛艳梅,董贵斌,等.FeSO4铵滴定法测定氯化稀土中氧化铈含量的方法研究[J].当代化工,2013,42(5):705-708.
[12]李良才.稀土提取及分离[M].包头:科学技术出版社,2011:448.
基本信息:
DOI：10.13355/j.cnki.sfyj.2016.04.012
中图分类号:X781;TF845.6
引用信息:
[1]许国华,赵军,刘磊,等.从氧化铈废料中回收稀土试验研究[J].湿法冶金,2016,35(04):324-326.DOI:10.13355/j.cnki.sfyj.2016.04.012.
2016-06-24
2016-06-24
2016-06-24