研究了常压下从铅阳极泥中碱浸脱砷,考察了浸出时间、浸出温度、NaOH质量浓度、H2O2添加量和液固体积质量比等对砷脱除及铅、锑浸出的影响。结果表明:在阳极泥质量50 g、浸出温度90℃、H2O2添加量10 mL、NaOH质量浓度60 g/L、液固体积质量比4 mL/1 g、浸出时间90 min条件下,砷浸出率为94.98%,而铅、锑基本不溶,砷脱除效果较好。
Abstract：The removal of arsenic by atmospheric alkaline leaching from lead anode slime was studied.The effects of leaching time, leaching temperature, NaOH concentration, H2O2 usage and ratio of liquid volume-to-solid mass on removal of arsenic were examined.The results show that under the conditions of anode slime mass of 50 g, temperature of 90 ℃,H2O2 usage of 10 mL,concentration of NaOH of 60 g/L,ratio of liquid volume-to-solid mass of 4 mL/1 g and raction time of 90 min, the removal of As reaches 94.98%,while Pb and Sb are not indissolvable.Arsenic is removed effectively from the anode slime.
[1] 何云龙.高铋铅阳极泥中有价金属分离与富集的应用基础研究[D].昆明：昆明理工大学，2018.
[2] 徐磊，阮胜寿.铅阳极泥湿法预处理的工业化试生产实践[J].中国有色冶金，2016,45(3):16-19.
[3] 李阔.高铋铅阳极泥脱砷锑工艺研究[D].昆明：昆明理工大学，2015.
[4] 林星杰.铅冶炼行业重金属污染现状及防治对策[J].有色金属工程，2011,1(6):23-27.
[5] 廖春发，邹耕，彭珊，等.从铜阳极泥分铜渣碱浸液中回收碲[J].湿法冶金，2021,40(2):120-124.
[6] 柯文帅.铅电解过程中杂质的行为分析及控制方法探讨[J].世界有色金属，2018(21):5-6.
[7] 王宝军.铅电解过程中影响析出铅结晶的因素[J].有色矿冶，2017,33(1):40-44.
[8] 陈思象，冯开行.高电流密度铅电解节能生产实践[J].中国有色冶金，2005,34(4):29-31.
[9] 周云峰，王少龙，李昌林，等.铅阳极泥脱砷预处理研究现状与进展[J].新技术新工艺，2011(10):67-69.
[10] 魏昶，姜琪，罗天骄，等.重有色金属冶炼中砷的脱除与回收[J].有色金属，2003,55(增刊1):46-50.
[11] 张国靖，李敦钫，吴昆华，等.高砷铅阳极泥处理新工艺的研究[J].有色金属(冶炼部分),1996(2):10-13.
[12] 蔡练兵，刘维，柴立元.高砷铅阳极泥预脱砷研究[J].矿冶工程，2007(6):44-47.
[13] 杨克儿，黄春霞，佟珊玲，等.从铅阳极泥中分离锑[J].湿法冶金，2005,24(2):108-111.
[14] 杨天足，水承静，宾万达.铅阳极泥湿法处理工艺述评[J].黄金，1996,17(11):33-38.
[15] 聂晓军，陈庆邦，刘如意.高锑低银铅阳极泥湿法提银及综合回收的研究[J].广东工学院学报，1996,13(4):51-57.
[16] 王文祥，王晓阳，孙雁军，等.高砷高锡铅阳极泥中有价金属的综合回收[J].有色金属(冶炼部分),2018(5):21-24.
[17] 方红生，李慧颖，王晓阳，等.高砷高锡铅阳极泥脱砷与综合回收工业试验[J].矿冶，2020,29(4):111-115.
[18] 王绍宇，秦庆伟，刘文科，等.用氢氧化钠溶液从澳斯麦特熔炼烟尘中选择性浸出砷锑铅锌[J].湿法冶金，2018,37(3):198-201.
[19] HE Y L,XU R D,HE S W,et al.Phi-pH diagram of As-N-Na-H2O system for arsenic removal during alkaline pressure oxidation leaching of lead anode slime[J].Transactions of Nonferrous Metals Society of China,2017,27(3):676-685.
[20] WU W H,WANG Z J,LIU J B.Hydrometallurgical pretreatment process for the recovery of valuable metals from the lead anode slime[J].Advanced Materials Research,2013,813:153-156.
[21] HE Y L,XU R D,HE S W,et al.Alkaline pressure oxidative leaching of bismuth-rich and arsenic-rich lead anode slime[J].International Journal of Minerals,Metallurgy and Materials,2019,26(6):689-700.
[22] CHEN Y M,LIU N N,YE L G,et al.A cleaning process for the removal and stabilisation of arsenic from arsenic-rich lead anode slime[J].Journal of Cleaner Production,2018,176:26-35.
基本信息:
DOI：10.13355/j.cnki.sfyj.2021.04.015
中图分类号:TF812
引用信息:
[1]喻小强,徐家聪,易勤等.高砷铅阳极泥常压碱浸脱砷试验研究[J].湿法冶金,2021,40(04):342-346.DOI:10.13355/j.cnki.sfyj.2021.04.015.
基金信息:
国家自然科学基金资助项目(51804136,52064021,52074136); 中国博士后科学基金资助项目(2019T120625,2019M652276); 江西省主要学科学术与技术带头人-青年人才培养计划项目(20204BCJL23031); 江西省杰出青年科学基金资助项目(20202ACB213002); 江西理工大学青年英才支持计划; 江西省青年井冈学者; 江西省博士后科研项目择优资助项目(2019KY09)